BMCRM e00178 Table 1.

Table 1. Electroanalytical characteristics of screen printed electrodes (SPE) modified with fCNT/TiO2 obtained in a 5 mM solution of potassium hexacyanoferrate. The potential values and peaks of oxidation and reduction of potassium ferricyanide are presented for a potential sweep rate of 50 mV/s. (fCNT – functionalized carbon nanotubes).

Electroanalytical characteristics	Electrodes
Electroanalytical characteristics	SPE/fCNT/TiO₂	SPE
E_Red, V (vs. Ag/AgCl)	0,169±0,017	0,087±0,008
E_Ox, V (vs. Ag/AgCl)	0,256±0,014	0,421±0,041
ΔE, V (vs. Ag/AgCl)	0,084±0,009	0,499±0,052
E_1/2, V (vs. Ag/AgCl)	0,213±0,015	0,167±0,018
I_Red, μA	-23,37±2,06	6,16±0,50
I_Ox, μA	24,97±1,82	5,00±0,48
S_{electroactive}, см²	0,1355	0,0024

Note. The relative standard deviation was estimated for at least three measurements (n = 3).